Solubility Characteristics and Slow-Release Mechanism of Nitrogen from Organic-Inorganic Compound Coated Urea
MetadataShow full item record
A soil incubation method was used to investigate the solubility characteristics and slow-release mechanism of organic-inorganic compound coated urea at temperature of 10, 20, and 30°C. The membrane microstructure with and without incubation was tested via scanning electron microscopy (SEM). Slow release of nitrogen (N) from different inorganic minerals was analysed by the activation energy from the nutrient solubility system. The rate of nitrogen solubility increased with temperature increasing. The first-order reaction kinetic equation described the solubility process of coated urea. The rate constant also increased with temperature increasing. Moreover, the SEM images showed that the microstructure of the coating layer changed into a flocculent structure and the number of tiny pores and holes on the membrane surface increased significantly with temperature increasing, which increased N solubility rate. The Arrhenius equation indicated that activation energy was closely related to during the solubility process; the activation energy was reduced with rising, which resulted in N solubility rate increasing. Overall, the N solubility rate of coated urea was affected by temperature.
Copyright © 2015 Hongtao Zou et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.